HEMPADUR 15553-11630
- IMPA 155530
- Contact Us
老人环氧底漆155530-11630(灰白)
HEMPADUR 15553-11630
Description
HEMPADUR 15553 is a two-component epoxy paint. It cures to a flexible, well adhering coating with good abrasion and impact resistance. Contains zinc phosphate. Cures down to
Area of use
As a primer for HEMPATEX, HEMPADUR and HEMPATHANE systems on hot dipped galvanized surfaces, aluminium and stainless steel in moderately corrosive environments. HEMPADUR 15553 is also suited when roughening of the surface is not possible. Please see surface preparation overleaf.
Segments
Protective, Marine
Availability
HEMPADUR 15553
15553: BASE 15557: CURING AGENT 98021
Description: HEMPADUR 15553 is a two-component epoxy paint. It cures to a flexible, we adhering coating with
good abrasion and impact resistance. Contains zinc phosphate. Cures down to
Recommended use: As a primer for HEMPATEX, HEMPADUR and HEMPATHANE systems on hot dipped galvanized
surfaces, aluminium and stainless steel in moderately corrosive environments. HEMPADUR 15553 is
also suited when roughening of the surface is not possible. Please see surface preparation overleaf.
Service temperature: Maximum, dry exposure only:
Certificates/Approvals: Approved as a low flame spread material when used as part of a predefined paint system. Please refer
to “Declaration of Conformity” on www.Hempel.com for further details.
Complies with EU Directive 2004/42/EC: subcategory j.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:
Shade nos/Colours: 11630 / Off-white.
Finish: Flat
Volume solids, %: 55 ± 1
2
Theoretical spreading rate:
Flash point:
Specific gravity:
Dry to touch: 3 approx. hour(s)
Fu y cured: 7 day(s)
VOC content:
Shelf life: 6 months for the BASE and 2 years for the CURING AGENT (stored in closed container) (
from time of production.
Shelf life is dependent on storage temperature. Shelf life is reduced at storage temperatures above
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas.
-
APPLICATION DETAILS:
Version, mixed product: 15553
Mixing ratio: BASE 15557: CURING AGENT 98021
3 : 1 by volume
Application method: Airless spray / Brush
Thinner (max.vol.): 08450 (5%) / 08450 (5%)
Pot life: 2 hour(s)
Nozzle orifice: 0.017 - 0.019 "
Nozzle pressure: 175 bar [2537.5 psi]
(Airless spray data are indicative and subject to adjustment)
Cleaning of tools: HEMPEL'S TOOL CLEANER 99610
Indicated film thickness, dry: 50 micron [2 mils]
Indicated film thickness, wet: 100 micron [4 mils]
Overcoat interval, min: see REMARKS overleaf
Overcoat interval, max: see REMARKS overleaf
Safety: Handle with care. Before and during use, observe a safety labels on packaging and paint containers,
consult HEMPEL Safety Data Sheets and fo ow a local or national safety regulations.
SURFACE PREPARATION: Stainless steel and aluminium: Remove oil and grease etc. thoroughly with suitable detergent.
Remove salts and other contaminants by high pressure fresh water cleaning. Roughening of the
surface is recommended for optimum adhesion.
Galvanised steel: Remove oil and grease, etc. with suitable detergent. Remove salt and other
contaminants by (high pressure) fresh water cleaning. Zinc salts (white rust) must be removed by high
pressure hosing combined with rubbing with a stiff nylon brush if necessary.
It is recommended to overcoat spray-metallised surfaces as soon as possible to avoid possible
contamination.
APPLICATION CONDITIONS: Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation.
At the freezing point and below be aware of the risk of ice on the surface, which wi hinder adhesion.
Use only where application and curing can proceed at temperatures above:
temperature of the surface must also be above these limits.
The temperature of the paint itself should be: 15
ventilation during application and drying.
SUBSEQUENT COAT: According to specification. HEMPADUR, HEMPATHANE, HEMPATEX
REMARKS:
VOC - EU Directive 2004/42/EC: Product As supplied 5 vol. % thinning Limit phase II, 2010
Not available.
1555311630
For VOC of other shades, please refer to Safety Data Sheet.
Application(s): Ammonium chloride or any other passivation agent should not be present on the surface when coating
the galvanized surface.
Water should not be used for cooling down the steel.
Cleaning of steel should not be initiated unless the steel temperature is below:
As the galvanized zinc layer may be porous it is recommended to apply a mist coat of diluted product,
a ow air to escape, and then apply a fu coat of the product a few minutes later.
Film thicknesses/thinning: May be specified in another film thickness than indicated depending on purpose and area of use. This
wi alter spreading rate and may influence drying time and overcoating interval. Normal range dry is:
50-80 micron/2.0-3.2 mils
Overcoating: Overcoating intervals related to later conditions of exposure: If the maximum overcoating interval is
exceeded, roughening of the surface is necessary to ensure intercoat adhesion.
Before overcoating after exposure in contaminated environment, clean the surface thoroughly with
high pressure fresh water hosing and a ow drying.
A specification supersedes any guideline overcoat intervals indicated in the table.
Environment Atmospheric, medium
Surface temperature:
Min Max Min Max Min Max
HEMPADUR 27 h Ext. 14 h Ext. 3 h Ext.
HEMPATEX 5 h 9 d 2 h 41/2 d
HEMPATHANE 27 h 90 d 14 h 45 d 3 h 10 d
NR = Not Recomended, Ext. = Extended, m = minute(s), h = hour(s), d = day(s)
Overcoating note: In case of overcoating with coating other than HEMPADUR, apply a (thin) additional coat of the
product withing the described directions for overcoating.
A completely clean surface is mandatory to ensure intercoat adhesion, especia y at long overcoating
intervals. Any dirt, oil, grease, and other foreign matter must be removed with suitable detergent
fo owed by (high pressure) fresh water cleaning. Salts to be removed by fresh water hosing. Any
degraded surface layer, as a result of a long exposure period, must be removed. Water jetting
may be relevant to remove any degraded surface layer and may also replace the above mentioned
cleaning methods when properly executed. Consult HEMPEL for specific advice if in doubt.
To check whether the quality of the surface cleaning is adequate, a test patch may be relevant.
Note: HEMPADUR 15553 For professional use only.
ISSUED BY: HEMPEL A/S
1555311630
HEMPADUR 15553
This Product Data Sheet supersedes those previously issued.
For explanations, definitions and scope, see “Explanatory Notes” available on www.hempel.com. Data, specifications, directions and recommendations
given in this data sheet represent only test results or experience obtained under controlled or specially defined circumstances. Their accuracy,
completeness or appropriateness under the actual conditions of any intended use of the Products herein must be determined exclusively by the Buyer
and/or User.
The Products are supplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unless
otherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, any liability, including but
not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct or consequential losses or damages arising
from the use of the Products as recommended above, on the overleaf or otherwise. Product data are subject to change without notice and become void
five years from the date of issue.
Date of issue: March 2014 Page: 3/3 Product Data Sheet